Technical Details of BOROFLOAT®
Thicknesses and dimensions
Standard thicknesses
| Thickness in mm (inch) | Tolerance in mm (inch) |
|---|---|
| 0.70 (0.027) | ± 0.05 (0.002) |
| 1.10 (0.043) | ± 0.05 (0.002) |
| 1.75 (0.069) | ± 0.05 (0.002) |
| 2.00 (0.079) | ± 0.05 (0.002) |
| 2.25 (0.089) | ± 0.05 (0.002) |
| 2.75 (0.108) | ± 0.10 (0.004) |
| 3.30 (0.130) | ± 0.20 (0.008) |
| 3.80 (0.150) | ± 0.20 (0.008) |
| 5.00 (0.197) | ± 0.20 (0.008) |
| 5.50 (0.216) | ± 0.20 (0.008) |
| 6.50 (0.256) | ± 0.20 (0.008) |
| 7.50 (0.295) | ± 0.30 (0.012) |
| 9.00 (0.354) | ± 0.30 (0.012) |
| 11.00 (0.433) | ± 0.30 (0.012) |
| 13.00 (0.512) | ± 0.30 (0.012) |
| 15.00 (0.590) | ± 0.40 (0.016) |
| 19.00 (0.748) | ± 0.50 (0.020) |
| 21.00 (0.827) | ± 0.70 (0.027) |
| 25.40 (1.000) | ± 1.00 (0.040) |
"Panel thickness is continuously measured during production using laser thickness measuring equipment.
Further thicknesses and tolerances are available on request."
Standard sizes
| Size | Thickness |
|---|---|
| 1,150 x 850 mm (45.3 x 33.5 in.) | 0.7 – 25.4 mm (0.027 to 1.000 in.) |
| 1,700 x 1,300 mm (66.9 x 51.2 in.) | 19.0 – 21.0 mm (0.748 to 0.827 in.) |
| 2,300 x 1,700 mm (90.5 x 66.9 in.) |
3.3 – 15.0 mm (0.130 to 0.590 in.) |
Standard sizes of BOROFLOAT® 33
Thermal
Thermal properties
- Specific heat capacity cp (20–100 °C): 0.83 kJ/(kg·K)
- Thermal conductivity λ (90 °C): 1.2 W/(m·K)
- Transformation temperature Tg* (according to ISO 7884): 525 °C
Maximum Operating Temperature
- For short-term usage (< 10 h): 500 °C
- For long-term usage (≥ 10 h): 450 °C
The CTE of BOROFLOAT® 33 is 3 times lower than the CTE of Soda-lime glass.
Optical
Optical index of refraction
| Wavelength λ (nm) | Refraction index n |
|---|---|
| 435.8 | 1.48015 |
| 479.9 | 1.47676 (nF’) |
| 546.1 | 1.47311(ne) |
| 589.3 | 1.47133 |
| 643.8 | 1.46953 (nC’) |
| 656.3 | 1.46916 |
Reference values, not guaranteed values.
Optical data
- Abbe number (ve = (ne – 1) / (nF‘ – nC‘)): 65.41
- Refraction index (nd (λ587.6 nm)): 1.47140
- Dispersion (nF – nC): 71.4 x 10-4
- Stress-optical coefficient (K): 4.0 x 10-6 mm2 N-1
Reference values, not guaranteed values.
Inherent fluorescence
Chemical
Chemical durability
- Hydrolytic resistance (according to ISO 719 / DIN 12 111): HGB 1
- Hydrolytic resistance (according to ISO 720): HGA 1
- Acid resistance (according to DIN 12 116): 1
- Acid resistance (according to ISO 1776): ≤ 100 μg Na₂O per 100 cm²
- Alkali resistance (according to ISO 695 / DIN 52 322): A 2
Resistance to selected chemicals
24 h at 95 °C:
| Reagent | Abrasion [mg/cm2] | Visual observations |
|---|---|---|
| H20 | < 0,01 | Unchanged |
| 5 Vol.% HCl | < 0,01 | Unchanged |
| 0,02 n H2S04 | < 0,01 | Unchanged |
6 h at 95 °C:
| Reagent | Abrasion [mg/cm2] | Visual observations |
|---|---|---|
| 5 % NaOH | 1,1 | White stains |
| 0,02 n NaOH | 0,16 | White haze |
| 0,02 n Na2CO3 | 0,16 | Unchanged |
20 min. at 23 °C:
| Reagent | Abrasion [mg/cm2] | Visual observations |
|---|---|---|
| 10 % HF | 1,1 | Stained white haze |
| 10 % NH4F x HF | 0,14 | Unchanged |
Chemical resistance of BOROFLOAT® 33 to selected reagents as a function of time and temperature.
Quantity of Na2O released from BOROFLOAT® 33 compared tosoda-lime glass depending on the temperature after 16 hours.
Compared to soda-lime glass, BOROFLOAT® 33 has a significantly higher hydrolytic resistance, because the number of sodium ions in the glass network is significantly lower with BOROFLOAT® 33. The few sodium ions are also more strongly bound.
Mechanical
Mechanical properties:
- Density ρ (25° C): 2.23 g/cm3
- Young´s Modulus E (according to DIN 13316): 64 kN/mm2
- Poisson's Ratio μ (according to DIN 13316): 0.2
- Knoop Hardness HK0.1/20 (according to DIN ISO 9385): 480
Vickers-Test
Mechanical resistance to penetration by a pointed object – BOROFLOAT® 33 is particularly resistant due to its glass structure.
PEI Abrasion Test
Transition from sliding abrasion to erosion (grain fill, loose grains) – BOROFLOAT® 33 is particularly abrasion resistant.